Once the aluminum scrap is collected and sorted, it is placed into a melting furnace and turned into molten aluminum at temperatures ranging from 1300 to 1400 degrees Fahrenheit. This molten aluminum cast into large slabs called ingots or billets. And since aluminum never loses its performance or strength during the recycling process, the same piece of aluminum can enter the secondary production process time and time again, multiplying the cost savings and environmental benefits. Not only does secondary aluminum production use less energy, it reduces landfill waste, contributes much lower greenhouse gas emissions and greatly reduces costly international transportation.

GROUP OF ALLOYS MARKING OF ALLOY CHEMICAL COMPOSITION OTHERS
Si Fe Cu Mn Mg Cr Ni Zn Pb Sn Ti Eatch Total
AlCu EN AB-21000 EN AB-AlCu4MgTi 0,15(0,20) 0,30(0,35) 4,2-5,0 0.10 0,20-0,35 _ 0.05 0.10 0.05 0.05 0,15-0,25 0.03 0.10
EN AB-21100 EN AB-AlCu4Ti 0,15(0,18) 0,15(0,19) 4,2-5,2 0.55 _ _ _ 0.07 _ _ 0,15-0,25 0.03 0.10
AlSiMgTi EN AB-41000 EN AB-AlSi2MgTi 1,6-2,4 0,50(0,60) 0,08(0,10) 0,30-0,50 0,50-0,65 _ 0.05 0.10 0.05 0.05 0,07-0,15 0.05 0.15
AlSi7Mg EN AB-42000 EN AB-AlSi7Mg 6,5-7,5 0,45(0,55) 0,15(0,20) 0.35 0,25-0,65 _ 0.15 0.15 0.15 0.05 0,05-0,20 0.05 0.15
EN AB-42100 EN AB-AlSi7Mg0,3 6,5-7,5 0,15(0,19) 0,03(0,05) 0.10 0,30-0,45 _ _ 0.07 _ _ 0,10-0,18 0.03 0.10
EN AB-42200 EN AB-AlSiMg0,6 6,5-7,5 0,15(0,19) 0,03(0,05) 0.10 0,50-0,70 _ _ 0.07 _ _ 0,10-0,18 0.03 0.10
AlSi10Mg EN AB-43000 EN AB-AlSi10Mg (a) 9,0-11,0 0,40(0,55) 0,03(0,05) 0.45 0,25-0,45 _ 0.05 0.10 0.05 0.05 0.15 0.05 0.15
EN AB-43100 EN AB-AlSi10Mg (b) 9,0-11,0 0,45(0,55) 0,08(0,10) 0.45 0,25-0,45 _ 0.05 0.10 0.05 0.05 0.15 0.05 0.15
EN AB-43200 EN AB-AlSi10Mg (Cu) 9,0-11,0 0,55(0,65) 0,30(0,35) 0.55 0,25-0,45 _ 0.15 0.35 0.10 _ 0,15(0,20) 0.05 0.15
EN AB-43300 EN AB-AlSi9Mg 9,0-10,0 0,15(0,19) 0,03(0,05) 0.10 0,30-0,45 _ _ 0.07 _ _ 0.15 0.03 0.10
EN AB-43400 EN AB-AlSi10Mg (Fe) 9,0-11,0 0,45-0,9 0,08(0,10) 0.55 0,25-0,50 _ 0.15 0.15 0.15 0.05 0,15(0,20) 0.05 0.15
Al Si EN AB-44000 EN AB-AlSi11 10,0-11,8 0,15(0,19) 0,03(0,5) 0.10 0.45 _ _ 0.07 _ _ 0.15 0.03 0.10
EN AB-44100 EN AB-AlSi12 (b) 10,5-13,5 0,55(0,65) 0,10(0,15) 0.55 0.10 _ 0.10 0.15 0.10 _ 0,15(0,20) 0.05 0.15
EN AB-44200 EN AB-AlSi12 (a) 10,5-13,5 0,40(0,55) 0,03(0,05) 0.35 _ _ _ 0.10 _ _ 0.15 0.05 0.15
EN AB-44300 EN AB-AlSi12 (Fe) 10,5-13,5 0,45-0,9 0,08(0,10) 0.55 _ _ _ 0.15 _ _ 0.15 0.05 0.25
EN AB-44400 EN AB-AlSi9 8,0-11,0 0,55(0,65) 0,08(0,10) 0.50 0.10 _ 0.05 0.15 0.05 0.05 0.15 0.05 0.15
AlSi5Cu EN AB-45000 EN AB-AlSi6Cu4 5,0-7,0 0,9(1,0) 3,0-5,0 0,20-0,65 0.55 0.15 0.45 2.00 0.30 0.15 0,20(0,25) 0.05 0.35
EN AB-45100 EN AB-AlSi5Cu3Mg 4,5-6,0 0,50(0,60) 2,6-3,6 0.55 0,20-0,45 _ 0.10 0.20 0.10 0.05 0,20(0,25) 0.05 0.15
EN AB-45200 EN AB-AlSi5Cu3Mn 4,5-6,0 0,7(0,8) 2,5-4,0 0,20-0,55 0.40 _ 0.30 0.55 0.20 0.10 0,15(0,20) 0.05 0.25
EN AB-45300 EN AB-AlSi5Cu1Mg 4,5-5,5 0,55(0,65) 1,0-1,5 0.55 0,40-0,65 _ 0.25 0.15 0.15 0.05 0,05-0,20 0.05 0.15
EN AB-45400 EN AB-AlSi5Cu3 4,5-6,0 0,50(0,60) 2,6-3,6 0.55 0.05 _ 0.10 0.20 0.10 0.05 0,20(0,25) 0.05 0.15
AlSi9Cu EN AB-46000 EN AB-AlSi9Cu3 (Fe) 8,0-11,0 0,6-1,1 2,0-4,0 0.55 0,15-0,55 0,15 0.55 1.20 0.35 0.25 0,20(0,25) 0.05 0.25
EN AB-46100 EN AB-AlSi11Cu2 (Fe) 10,0-12,0 0,45-1,0 1,5-2,5 0.55 0.3 0,15 0.45 1.70 0.25 0.25 0,20(0,25) 0.05 0.25
EN AB-46200 EN AB-AlSi8Cu3 7,5-9,5 0,7(0,8) 2,0-3,5 0,15-0,65 0,15-0,55 _ 0.35 1.20 0.25 0.15 0,20(0,25) 0.05 0.25
EN AB-46300 EN AB-AlSi7Cu3Mg 6,5-8,0 0,7(0,8) 3,0-4,0 0,20-0,65 0,35-0,60 _ 0.30 0.65 0.15 0.10 0,20(0,25) 0.05 0.25
EN AB-46400 EN AB-AlSi9Cu1Mg 8,3-9,7 0,7(0,8) 0,8-1,3 0,15-0,55 0,30-0,65 _ 0.20 0.80 0.10 0.10 0,10-0,18 0.05 0.25
EN AB-46500 EN AB-AlSi9Cu3 (Fe) 8,0-11,0 0,6-1,2 2,0-4,0 0.55 0,15-0,55 0.15 0.55 3.00 0.35 0.25 0,20(0,25) 0.05 0.25
EN AB-46600 EN AB-AlSi7Cu2 6,0-8,0 0,7(0,8) 1,5-2,5 0,15-0,65 0.35 _ 0.35 1.00 0.25 0.15 0,20(0,25) 0.05 0.15
AlSi(Cu) EN AB-47000 EN AB-AlSi12 10,5-13,5 0,7(0,8) 0,9(1,0) 0,05-0,55 0.35 0,10 0.30 0.55 0.20 0.10 0,15(0,20) 0.05 0.25
EN AB-47100 EN AB-AlSi12Cu1 (Fe) 10,5-13,5 0,6-1,1 0,7-1,2 0.55 0.35 0.10 0.30 0.55 0.20 0.10 0,15(0,20) 0.05 0.25
AlSiCuNiMg EN AB-48000 EN AB-AlSi12CuNiMg 10,5-13,5 0,6(0,7) 0,8-1,5 0.35 0,9-1,5 _ 0,7-1,3 0.35 _ _ 0,20(0,25) 0.05 0.15
AlMg EN AB-51000 EN AB-AlMg3 (b) 0,45(0,55) 0,45(0,55) 0,08(0,10) 0.45 2,7-3,5 _ _ 0.10 _ _ 0,15(0,20) 0.05 0.15
EN AB-51100 EN AB-AlMg3 (a) 0,45(0,55) 0,45(0,55) 0,03(0,05) 0.45 2,7-3,5 _ _ 0.10 _ _ 0,15(0,20) 0.05 0.15
EN AB-51200 EN AB-AlMg9 2.5 0,45-0,9 0,08(0,10) 0.55 8,5-10,5 _ 0.10 0.25 0.10 0.10 0,15(0,20) 0.05 0.15
EN AB-51300 EN AB-AlMg5 0,35(0,55) 0,45(0,55) 0,05(0,10) 0.45 4,8-6,5 _ _ 0.10 _ _ 0,15(0,20) 0.05 0.15
EN AB-51400 EN AB-AlMg5(Si) 1,3(1,5) 0,45(0,55) 0,03(0,05) 0.45 4,8-6,5 _ _ 0.10 _ _ 0,15(0,20) 0.05 0.15
AlZnMg EN AB-71000 EN AB-AlZn5Mg 0,25(0,30) 0,70(0,80) 0,15-0,35 0.40 0,45-0,70 0,15-0,60 0.05 4,5-6,0 0.05 0.05 0,12-0,20 0.05 0.15
TURKEY INTERNATIONAL RENK RENK RENK
DM1 AlSi9Cu3 (Fe) / EN AC-46000 226D
DM2  AlSi12 (Fe) / EN AC-44300  230D
DM3  AlSi12Cu1 (Fe) / EN AC-47100  231D
DM4  AlSi10Mg (Fe) / EN AC-43400  239D
 –  AlSi8Zn15Mg  Si158
 Silumin Delta  –
 AlMg5Si2Mn  Magsimal-59
AlSi9Mg  Silafont-36
ASTM. 10.5Si-2.5Cu  A03830
No Si (Silisyum) Fe (Demir)  Cu (Bakır) Mn (Mangan) Mg (Magnezyum)  Zn (Çinko) Ni (Nikel) Cr (Krom) Pb (Kurşun) Sn (Kalay) Ti (Titanyum) Others Total Al
 1  8 – 11  1.3 (0.6-1.1)  2 – 3.5  0.55  0.05 – 0.5 (0.15 – 0.55)  1.2  0.3  0.15  0.35  0.25  0.25 (0.2)  0.05  0.25  Kalan
 2  10.5 – 13.5  1 (0.45 – 0.9)  0.1 (0.08)  0.55  –  0.15  –  –  –  –  0.15  0.05  0.25  Kalan
 3  10.5 – 13.5  1.3 (0.6 – 1.1)  0.7 – 1.2   0.55  0.35  0.55  0.3  0.1  0.2  0.1  0.20 (0.15)  0.05  0.25  Kalan
 4  9 – 11  1 (0.45 – 0.9)  0.1 (0.08)   0.55  0.2 – 0.5 (0.18 – 0.25) (Özel)  0.15  0.15  –  0.15  0.05   0.20 (0.15)  0.05  0.15  Kalan
 5  7.5 – 8.5  0.6  0.5  0.4  0.5  14 – 16  –  –  –  –  –  –  –  Kalan
 6  9 – 10.5  0.3 – 0.4  0.02  0.3 – 0.4  < 0.03  0.07  –  –  –  –  0.15  0.03  0.10  Kalan
 7  1.8 – 2.5  0.2  0.05  0.5 – 0.8  5 – 6  0.07  –  –  0.004  –  0.2  –  0.20  Kalan
 8  9.5 – 11.5  0.15  0.03  0.5 – 0.8  0.1 – 0.5  0.08  –  –  –  –  0.04-0.15  –  0.10  Kalan
 9  9 – 11.5  0.7 – 1.1  2 – 2.5  0.5  0.24  3.4 – 3.8  0.3  –  0.3  0.2  0.2  0.05  0.5  Kalan